| Recommended Cold Shearing Limitations for Cold Shearing Quality Hot Rolled Alloy and Carbon Steel Billets and Bars | ||||||||
| (Standard AISI & SAE Grades and Formerly Standard SAE Grades) | ||||||||
| Maximum Square or Equivalent Cross-Sectional Areaa After Cold Shear Annealing | ||||||||
| Grade Series Designation | When Maximum of Specified Carbon Range is, Percent | |||||||
| To 0.20 Incl. |
Over 0.20 To 0.25 Incl. |
Over 0.25 To 0.33 Incl. |
Over 0.33 To 0.44 Incl. |
Over 0.44 To 0.49 Incl. |
Over 0.49 To 0.55 Incl. |
Over 0.55 To 0.76 Incl. |
Over 0.76 To 1.05 Incl. |
|
| lOXX, 12XX and 11XX thru 1.00 max Mn | 6 1¼ | 6 1¼ | 6 | 5 | 4 1¼ | 4 | 3 1¼ | 2 1¼ |
| llXX over 1.00 max Mn and 15XX | 6 1¼ | 6 | 5 1¼ | 4 1¼ | 4 | 3 | 2 1¼ | — |
| 13XX | — | 5 | 4 3¼ | 4 1¼ | 4 | — | — | — |
| 23XX | 5 | 5 | 4 3¼ | 4 1¼ | 3 1¼ | — | — | — |
| 25XX | 5 | — | — | — | — | — | — | — |
| 31XX | 5 | 5 | 4 3¼ | 4 1¼ | 4 | — | — | — |
| 32XX | 4 | 3 1¼ | 3 | 2 1¼ | a | — | — | — |
| 33XX | 3 | — | a | a | a | — | — | — |
| 34XX | 4 1¼ | — | — | 3 | — | — | — | — |
| 40XX | 5 | 5 | 4 3¼ | 4 1¼ | 4 1¼ | 4 1¼ | a | — |
| 41XX | 5 | 5 | 4 3¼ | 4 1¼ | 4 | 3 | — | — |
| 43XX | 4 3¼ | 4 3¼ | — | 4 | — | — | — | — |
| 44XX | — | 5 | 4 3¼ | — | — | — | — | — |
| 46XX | 5 | 5 | 4 3¼ | 4 1¼ | — | — | — | — |
| 47XX | — | 5 | — | — | — | — | — | — |
| 48XX | 5 | 4 3¼ | — | — | — | — | — | — |
| 50XX | 5 | — | — | — | 4 1¼ | — | — | — |
| 50BXX | — | — | — | 4 1¼ | 4 1¼ | 3 1¼ | a | — |
| 51XX | 5 | 5 | 4 3¼ | 4 1¼ | 4 | 3 1¼ | — | — |
| 51BXX | — | — | — | — | 4 | 3 1¼ | a | — |
| 61XX | 5 | 5 | 4 3¼ | 4 1¼ | 4 | 3 | — | a |
| 81XX | 5 | — | — | — | — | — | — | — |
| 81BXX | — | — | — | — | 4 | — | — | — |
| 86XX | 5 | 5 | 4 3¼ | 4 1¼ | 4 | 3 1¼ | a | — |
| 86BXX | — | — | 4 3¼ | — | 4 | — | — | — |
| 87XX | — | — | — | 4 1¼ | 4 | 3 1¼ | — | — |
| 88XX | — | 4 3¼ | — | — | — | — | — | — |
| 92XX | — | — | — | — | — | 1 | a | — |
| 93XX | 3 | — | — | — | — | — | — | — |
| 94XX | — | — | — | 4 1¼ | 4 | 3 1¼ | — | — |
| 94BXX | 5 | — | 4 3¼ | 4 1¼ | — | — | — | — |
| 97XX | — | — | — | — | — | 3 1¼ | a | — |
| 98XX | — | — | — | 3 3¼ | 3 | a | — | — |
| 43BVXX | 4 3¼ | — | — | — | — | — | — | — |
| NOTE: | For standard H grades, the maximum carbon content of the comparable standard steel is used when considering cold shearing limitations. |
| a | All sizes in this carbon range should be thermally treated before cold shearing. |
| b | Refer to Table 1-4 for cross-sectional area and metric equivalents. |